A study of the microstructure and wear of high speed steels

El-Rakayby, AM 1986, A study of the microstructure and wear of high speed steels , PhD thesis, University of Salford.

PDF - Submitted Version
Download (11MB) | Preview


The present work describes the successful extraction of the secondary hardening carbides of high speed steels, which allowed the identification of these carbides by crystalloqraphic, and microanalysis techniques. The secondary hardening carbide of high speed steels was found to be the-cubic M2C carbide and not the MC carbide as previously claimed. The secondary kic carbide was found to precipitate in the over-tempered state well beyond peak hardness. The sequence of secondary carbide precipitation has been determined. The relation between wear resistance and hardness of high speed steels has been found to be non-linear due to microstructural changes at and beyond peak hardness. However, primary carbides of the MC and M6C types of carbides were found to be stable during tempering, of these steels. It has been shown that the primary carbides did not contribute to the wear resistance of steels tempered to peak hardness. -However, the primary carbides were found to contribute to the wear rate of over-tempered steels due to their abrasive role.

Item Type: Thesis (PhD)
Contributors: Mills, B (Supervisor)
Themes: Subjects outside of the University Themes
Schools: Schools > School of Computing, Science and Engineering
Depositing User: Institutional Repository
Date Deposited: 16 Aug 2011 15:38
Last Modified: 19 Oct 2021 10:32
URI: http://usir.salford.ac.uk/id/eprint/14825

Actions (login required)

Edit record (repository staff only) Edit record (repository staff only)


Downloads per month over past year